mine is dry pulsed etc to the point that it changes colour. It is spot on in resistance and tcr (as far as I can tell). I havent tried a coil without dry pulsing but I will...stay tuned!
SXmini M Class (TEMP CONTROL)
- Thread starter whitewidows
- Start date
- th_trl_thread_readers 0
- Status
Don't think that a good idea. That's what I warned against (legs snapping when no dry-burning) when you said you did not understand. But, let's hear your result.
sorry so you were saying dry burning is essential??? Even for a spaced coil for example??
Yes. It was the spaced coil legs that snapped.
May not be true for some attys but the small build area and TINY screws on the GEM snapped, at some point, on everyone of my 52 builds.
Go for it though. Ignore my experience. [emoji12]
this local guy made me some ss claptons, multi-braid. not sure where he got it or even what type it is. it is strange I find every coil needs way more aggressive settings on the dna200. at least it can serve it up. the sxmm just gives me a better vape. that's just my opinion but I have had both for a while. I do not think the ml is going to be ground breaking and I doubt they fix the paint. I will keep the trusty m class. looks like crud but continues to perform. I am not sure I could break it if I tried.
as for ss wire I am sure I saw it on a site but don't remember where now. the rda screws took me 2 hours but I will not accept that I am disabled.
as for ss wire I am sure I saw it on a site but don't remember where now. the rda screws took me 2 hours but I will not accept that I am disabled.
You know everytime I use this SXMM I still cannot believe how well it works with Ti1 wire. I just set it for Ti01 mode lock in resistance set my comp temp to 22C approx home temp set it to 410 14-15J on a .28ohm coil and it is perfect. I am just really impressed.
You must mean NiFe 48, right?
1. Go into the Menu to Coil Select
2. Choose Manual TCR
3. Set the TCR to 0.00405
4. Hit the fire button
You can set the Resistance before or after in the usual way.
A setting for Room Temp will appear. The Default is 20 C. Use that or adjust for your actual room temp: 21, 22, 23 C &etc.
From the "TC Beyond Ni 200..." Thread
balazsk
Full Member
@jazzvaper I will try to collect the TCR for all the known wires.
Stainless steel types:
317: 0.000875
316: 0.000915
304: 0.00105
430: 0.00138
410: 0.00155 - this value hasn't been verified yet
NiFe alloys:
Pernifer36(Invar): 0.00117
Resistherm(Dicodes): 0.0032
Nifethal52(NiFe48 at Zivipf): 0.00405
Nifethal70(NiFe30 at Zivipf): 0.00506
Ni200: 0.0052 (20°C-200°C)
Titanium #1: 0.0035
(Niobium: 0.0028 - not verified
I got around to trying 316L stainless tonight. Should I be pulsing these? I tried 5 wrap 28g 2.5mm micro coil without pulsing and it was clearly not operating correctly. It seemed like it was running way to hot and was boiling and spitting juice like I have never seen before. The next coil I pulsed multiple times at 12w until the coils were firing from the middle out consistently. This coil seems to be working fine and the TC is working similar to ni200. I have the TCR set to 0.00092 with an offset of 22 and my room temp is 70. Does this sound about right on the SX Mini M class using 316L?
^^^^ Sounds right. And yes, you should dry-burn SS before vaping it. The behavior you mention is precisely what happens w/o dry-burning. (I have a standing challenge, "Until somebody proves me wrong. [emoji15])
Just built my first coil but in the TCR Menu, I can only select Ni200 or Ti. There is no option for manual selection. I have the latest beta software but maybe I am doing something wrong?
Anyway, on my OHMs meter it's reading 0.3ohms (3mm 6 wrap 26guage) Any tips on getting manual mode working much appreciated
Anyway, on my OHMs meter it's reading 0.3ohms (3mm 6 wrap 26guage) Any tips on getting manual mode working much appreciated
- Status